Weld failure analysis of 2205 duplex stainless steel nozzle

Publié le par
Répondre

A publication in « Case Studies in Engineering Failure Analysiss, october 2014.

Failure analyses of weld joint between the nozzle and the head of the reactor made of 2205 duplex stainless steel was performed by optical microscopy (OM) and scanning electron microscopy (SEM). Cracks were found in HAZ of the weld. The depth of the cracks is equal to the thickness of the inner weld. Localized uneven distribution of ferrite/austenite with 80-90% ferrite in weld is found. Results show that the cracks occurred along columnar granular with cleavage fracture. Poor weld process probably results in these cracks.

Source : Case Studies in Engineering Failure Analysis

Failure analysis of interfering part of a steam turbine journal bearing

Publié le par
Répondre

An article published in « Case Studies in Engineering Failure Analysis« , octobre 2014.

Journal bearings as so sensitive parts of steam turbines are very susceptible to failure through different mechanisms of wear, fatigue and crush during service conditions. Failure occurring through these mechanisms lead to turbine completely shut down as a result of interfering in working conditions of bearing different parts. In this paper, failed interfered part of a journal bearing related to a 320,000 kW steam turbine was examined. The studies were revealed that the bearing part loosing and inappropriate clearance can produce relative displacements under cyclic gradient loading. This condition was detrimental for the service life of turbine journal bearing via failure through fretting fatigue mechanism.

Read more

Failure analysis of re-bars during bending operations

Publié le par
Répondre

Failure_analysis_of_Rebar

An article published in « Case Studies in Engineering Failure Analysis« , october 2014.

This  paper highlights failure investigation of a failed rebar during bending operations. From fractography and microstructural analysis it is confirmed that the rebar sample failed in brittle manner due to through harden martensitic structure and which indicates that there is some anomaly in water box resulting in these premature failures.

Read more

Cas Concrets – Des ruptures de fatigue en flexion

Publié le par
Répondre

Avatar Cas ConcretsLe mode de sollicitation en service influe sur la morphologie des faciès de cassure. Les quatre cas de ruptures par fissuration progressive en fatigue en flexion plane et rotative illustrent ce propos. Ces quatre fiches d’analyse de défaillance avaient été publiées en 1981 et 1982 dans la revue Cetim-information. Des dizaines de milliers de cas ont été traités ces quarante dernières années par le Cetim. Cette expérience fait du Centre une référence dans le domaine à même d’intervenir dans tous les secteurs d’activités. Avec aujourd’hui ses centres associés et partenaires, l’Institut technologique Cetim met un ensemble de compétences et de moyens au service des industriels et experts pour analyser, comprendre et proposer des solutions permettant d’éviter la reproduction de ces défaillances. Les différentes expertises de cette série « Cas concrets » sont issues d’articles publiés dans la revue Cetim Informations dans les années 74 à 90. Bien que ces fiches traitant de cas concrets soient anciennes, leur contenu est toujours d’actualité…

Source : Cas Concrets – Des ruptures de fatigue en flexion – Cetim – Centre technique des industries mécaniques

Cas Concrets – Des ruptures brutales

Publié le par
1

Avatar Cas ConcretsQuatre fiches de cas d’analyses de défaillances survenues en service : une pièce de jonction en acier, un extincteur à gaz en alliage d’aluminium, une pièce d’attelage en acier mécano soudé et un essieu directeur de chariot élévateur, peuvent être consultées dans la Mécatech du Cetim.

telecharger le doc

 

Understanding the Effects of Hydrogen on SCC of Pipelines

Publié le par
Répondre

A thesis submitted in Department of Chemical and Materials Engineering University of Alberta, © Zeynab Shirband, 2016.

Near-neutral pH stress corrosion cracks (NNpH SCC) are developed under coating disbondments on the external surface of pipelines where the surface of pipeline is exposed to the soil solution. NNpH SCC initiation and early stage of growth is mainly governed by the dissolution process of steel. …This study aimed at understanding the contribution of these important factors to NNpH SCC. In this study, the role of coating disbondment on hydrogen ingress into pipeline steels and the effects of mill-scale and hydrotesting on NNpH SCC crack initiation are investigated.

Read more

Abrasive Wear Failure Analysis of Tungsten Carbide Hard facing on Carbon Steel Blade

Publié le par
Répondre

This content has been downloaded from IOPscience, Series: Materials Science and Engineering 165 (2017),

This study investigate the abrasive wear failure of tungsten carbide hardfacing on continuous digester (CD) blade (carbon steel) in an environment of sulphuric acid and ilmenite ore mixture. Comparison being made on the hardness, thickness and microstructural of the hardfacing between unworn and 3 months old worn blade on few locations around the blade. The cross sections of the blade revealed non-uniform coverage of the hardfacing on the blade for both worn and unworn blade. The edge of the blade has the least amount of hardfacing thickness which with time acts as the point of failure during the wear process. The hardness obtained from both the unworn and worn samples are around 25% lower from the hardfacing electrode manufacturer’s hardness specification. Microstructural micrograph analysis of the hardfacing reveale

Read more

Une base de données « Matériaux – Fatigue » au Cetim

Publié le par
Répondre

cetim_donnee_fatigue_materiaux

Les industriels de différentes professions (Transmissions mécaniques, Machinisme agricole et Moteurs compresseurs) ont souhaité avoir une base de données en fatigue pour un certain nombre de matériaux.

Les caractéristiques mécaniques statiques et de fatigue sont 17reportées pour chaque matériau sous forme de fiches. Ces fiches permettent ainsi à l’utilisateur un accès rapide à l’information et peuvent être utilisées dans le cadre du dimensionnement en fatigue de ses pièces.

Source : Données « Matériaux – Fatigue » – Cetim – Centre technique des industries mécaniquescetim_cotenu-reserve-cotisants

Concerns of corrosive effects with respect to lightning protection systems

Publié le par
Répondre

An interesting  paper published in  » Engineering Failure Analysis » on www.sciencedirect.com, Volume 57, November 2015.

Lightning protection system elements need to be selected from materials which are resistant to corrosion and should be protected from fast degradation. However, over the time corrosion will take place in the presence of galvanically dissimilar metals in the same electrolyte (moisture)……

This paper presents the causes of corrosion and recent developments in minimising the corrosion associated with lightning protection and grounding systems.

Read more

Déjouez les pièges de la corrosion à Toulouse le 18 mai

Publié le par
Répondre

Une « Journée Technique » du Cetim à Toulouse le 18 mai.

La corrosion reste un mal industriel majeur. Et ce, en dépit des avancées scientifiques et des progrès technologiques continus. Elle est encore aujourd’hui responsable d’un grand nombre d’avaries et touche de nombreux domaines.Elle revêt différentes formes et un cas apparemment simple peut cacher un phénomène complexe. Ses causes étant multiples, sa détection, sa mesure et sa maîtrise relèvent de compétences variées qui en font une affaire de spécialistes !

Ayez les bons réflexes et venez profitez de l’expertise du Cetim à l’occasion de cette journée, qui vous aidera à déjouer les pièges de la corrosion.

Pour savoir plus et s’inscrire : Journees-techniques/Corrosion