Failure Analysis of Work Rolls of a Thin Hot Strip Mill

Publié le par
Répondre

A new interesting article published in « Case Studies in Engineering Failure Analysis »

In hot rolling mills, premature failure of rolls is a major concern as it adversely affects the mill operation and as well as production. Analysis of failed roll materials and actual rolling conditions in service are therefore necessary to understand the roll failure mechanism and thereby improve the wear resistance and extend the service life of rolls.

This work describes two different types of roll failure cases and their analysis which was carried out using destructive as well as non-destructive testing techniques (NDT). The cases are as follows:

(a)

Case I: Enhanced ICDP Bottom roll of fifth stand (F#5) which failed from the neck portion.

(b)

Case II: Analysis of sub-surface defect of ICDP rolls of the last stand (F#6

Lire la suite

 

Textes des conférences de la 5ème édition, Fatigue Design, 2013

Publié le par
Répondre

2015-02-01_11h28_58 Les textes des conférences de la 5 e édition, Fatigue Design, la conférence internationale de la conception vis-à-vis de la fatigue, sont en ligne sur SciencDirect.com. Biennale reconnue et attendue de la conception vis-à-vis de la fatigue, le Congrès international Fatigue Design a rassemblé plus de 300 personnes au Cetim à Senlis les 27 et 28 novembre 2013 Cette conférence internationale présente les démarches innovantes et les avancées scientifiques de la conception en fatigue à la prolongation des durées de vie. Au cœur de ces journées : les applications industrielles. Les thèmes habituels sont évidemment au programme de ces deux journées avec : la fatigue des assemblages soudés qui associe approche expérimentale et simulation numérique, les chargements complexes qui intéressent les industriels des domaines du transport, de l’énergie, mais aussi des laboratoires internationaux spécialisés dans le domaine de la fatigue. Au sommaire également : la prise en compte des paramètres du procédé d’élaboration des matériaux pour obtenir les caractéristiques en fatigue attendues par les industriels. Sont concernés notamment, les aciéristes désireux de maîtriser le comportement à la fatigue de leurs produits. Parmi les autres thèmes récurrents, citons : les méthodes expérimentales de la fatigue (« fatigue testing »), et la propagation des fissures par fatigue.

Accéder aux articles en ligne

Failure analysis of the pulleys during the press-fit assembling process

Publié le par
Répondre

A case study published in « Case Studies in Engineering Failure Analysis« .

This article highlights failure investigation of the pulleys during a press-fit assembling process. Pulleys are used to transmit power between rotational mechanical elements. Failure analysis was found that cooperative influence of higher carbon content with combination of elongated sulphides is reason for pulleys cracking. Steel cleanliness and homogeneous structure is an important factor for users of steel. The success of production process is connected with the optimal quality of steel.

Click here to read more

 

A study of the wear mechanisms of disk and shoe brake pads

Publié le par
Répondre

Un article paraître dans le numéro de fin janvier de la revue « Engineering Failure Analysis« . Il traite d’un cas d’analyse de défaillance d’un ensemble disque-mâchoire de frein usé en service.

Vous rencontrez un cas similaire, n’hésitez à pendre contact avec les experts en tribologie du Cetim. 11

Failure analysis of work rolls of a thin hot strip mill

Publié le par
Répondre

A new case study of failure analysis published on Sciencedirect.com

In hot rolling mills, premature failure of rolls is a major concern as it adversely affects the mill operation as well as production. Analysis of failed roll materials and actual rolling conditions in service are therefore necessary to understand the roll failure mechanism and thereby improve the wear resistance and extend the service life of rolls.

The hot strip mill referred here consists of six stands wherein high chromium (Hi-Cr) iron rolls and Indefinite Chilled Double Poured (ICDP) cast iron rolls are being used for finishing rolling of the strips in the last two stands. The thin strip mill produces strips in the thickness range of 1.0–12.7 mm. This work describes two different types of roll failure cases and their analysis which was carried out using destructive as well as non-destructive testing techniques (NDT).

Read More

Fissure sur une drague du port autonome de Nantes-St-Nazaire

Publié le par
Répondre

Une fissure importante découverte sur la drague André Gendre du Port Autonome de Nantes Saint-Nazaire a obligé les équipes techniques à réagir vite lors de sa mise à sec. Elles ont fait appel au Cetim.
Pour en savoir plus, lire l’article en cliquant ici

 

Failure analysis of Co–Cr hip resurfacing prosthesis during solidification

Publié le par
Répondre

A paper published on january 2013 in « Case Studies in Engineering Failure Analysis« .

In this study a failure originated during solidification process into the femoral stem component of Hip Resurfacing prosthesis was investigated.  The results exhibited hot tearing, shrinkage porosity and metal oxide films due to inadequate heat dissipation during solidification process, as a consequence of poor investment casting ceramic mold configuration. Also in this paper was improved the casting design solving this kind of defects.

Read more

Use of Aerospace Fasteners in Mechanical and Structural Applications

Publié le par
Répondre

Hugh Magma lockUn article paru dans «  Annals of Materials Science & Engineering« , publié sur www.austinpublishinggroup.com

Abstract. The intention of the present short review is to introduce to the non-specialist reader the feasibility of the use of alternative materials not generally considered by engineers working in mechanical and structural applications. That is, the use of specialised aerospace rivets in the more general area of construction is considered. To this end, the text briefly overviews the different types of fasteners used in the construction industry and their common mechanisms of failure.

Une proportion importante des défaillances mécaniques sont liées à des problèmes d’assemblage. Vissage, soudage, rivetage, collage… aucun type n’est épargné.

Le Cetim traite pour sa part, plus d’une centaine de cas d’analyses de défaillance liés à cette problématique par an.

Erreurs de conception, problèmes de procédés ou de mise en œuvre d’assemblage, défauts de matière, sont autant de pistes à explorer pour identifier et localiser les origines du problème. Des solutions correctives et pérennes appropriées sont ensuite proposées et mises en œuvre. Les experts du Cetim se tiennent à votre disposition pour vous apporter conseils et expertises dans cette problématique. N’hésitez pas à les contacter : cliquez ici.

 

Flywheel Starter Ring Gear Failures

Publié le par
Répondre

A new case study in failure analysis published by ScienceDirect.com. This technical paper summarizes the case study conducted for truck flywheel starter ring gears with diameter of 470 mm in order to reduce hardness variation by optimization of induction hardening and tempering processes.

 