In vivo shell-like fractures of veneered-ZrO2 fixed dental prostheses

Publié le par
Répondre

A non commum case study of failure analysis published in october 2014 in « Case Studies in Engineering Failure Analysis« .

Fractographic analyses are performed in two fixed dental prosthetic reconstructions made of ZrO2 frameworks covered by a veneering ceramic that fractured during function in the mouth. Internal thermal residual stresses and occlusal surface defects from localized contact overloading were found to precipitate the fracture in Case 1, whereas extreme occlusal surface damage from sliding chewing contact was determinant in the fracture of Case 2. The interface between the veneering ceramic and the ZrO2 framework was unaffected by the fractures.

Source : In vivo shell-like fractures of veneered-ZrO2 fixed dental prostheses

Grooving corrosion of seam welded oil pipelines

Publié le par
Répondre

A paper published in « Case Studies in Engineering Failure Analysis« , october 2014.

24” pipeline carrying oil was failed in the form of longitudinal crack at the 6 O’clock position resulting in oil spill. The failed pipe was investigated to reveal the main cause of its failure. The procedure of investigation was built on studying the intact pipe, rupture area, parent material, and intact weld. Cracks were originated from weld defected sites, initiated by grooving corrosion, propagated by inertia at the normal designed pressure condition, and stopped when stress relief is attained.

Source : Grooving corrosion of seam welded oil pipelines

Cas Concrets – Des ruptures de fatigue en flexion

Publié le par
Répondre

Avatar Cas ConcretsLe mode de sollicitation en service influe sur la morphologie des faciès de cassure. Les quatre cas de ruptures par fissuration progressive en fatigue en flexion plane et rotative illustrent ce propos. Ces quatre fiches d’analyse de défaillance avaient été publiées en 1981 et 1982 dans la revue Cetim-information. Des dizaines de milliers de cas ont été traités ces quarante dernières années par le Cetim. Cette expérience fait du Centre une référence dans le domaine à même d’intervenir dans tous les secteurs d’activités. Avec aujourd’hui ses centres associés et partenaires, l’Institut technologique Cetim met un ensemble de compétences et de moyens au service des industriels et experts pour analyser, comprendre et proposer des solutions permettant d’éviter la reproduction de ces défaillances. Les différentes expertises de cette série « Cas concrets » sont issues d’articles publiés dans la revue Cetim Informations dans les années 74 à 90. Bien que ces fiches traitant de cas concrets soient anciennes, leur contenu est toujours d’actualité…

Source : Cas Concrets – Des ruptures de fatigue en flexion – Cetim – Centre technique des industries mécaniques

Cas Concrets – Des ruptures brutales

Publié le par
1

Avatar Cas ConcretsQuatre fiches de cas d’analyses de défaillances survenues en service : une pièce de jonction en acier, un extincteur à gaz en alliage d’aluminium, une pièce d’attelage en acier mécano soudé et un essieu directeur de chariot élévateur, peuvent être consultées dans la Mécatech du Cetim.

telecharger le doc

 

Abrasive Wear Failure Analysis of Tungsten Carbide Hard facing on Carbon Steel Blade

Publié le par
Répondre

This content has been downloaded from IOPscience, Series: Materials Science and Engineering 165 (2017),

This study investigate the abrasive wear failure of tungsten carbide hardfacing on continuous digester (CD) blade (carbon steel) in an environment of sulphuric acid and ilmenite ore mixture. Comparison being made on the hardness, thickness and microstructural of the hardfacing between unworn and 3 months old worn blade on few locations around the blade. The cross sections of the blade revealed non-uniform coverage of the hardfacing on the blade for both worn and unworn blade. The edge of the blade has the least amount of hardfacing thickness which with time acts as the point of failure during the wear process. The hardness obtained from both the unworn and worn samples are around 25% lower from the hardfacing electrode manufacturer’s hardness specification. Microstructural micrograph analysis of the hardfacing reveale

Read more

Concerns of corrosive effects with respect to lightning protection systems

Publié le par
Répondre

An interesting  paper published in  » Engineering Failure Analysis » on www.sciencedirect.com, Volume 57, November 2015.

Lightning protection system elements need to be selected from materials which are resistant to corrosion and should be protected from fast degradation. However, over the time corrosion will take place in the presence of galvanically dissimilar metals in the same electrolyte (moisture)……

This paper presents the causes of corrosion and recent developments in minimising the corrosion associated with lightning protection and grounding systems.

Read more

Déjouez les pièges de la corrosion à Toulouse le 18 mai

Publié le par
Répondre

Une « Journée Technique » du Cetim à Toulouse le 18 mai.

La corrosion reste un mal industriel majeur. Et ce, en dépit des avancées scientifiques et des progrès technologiques continus. Elle est encore aujourd’hui responsable d’un grand nombre d’avaries et touche de nombreux domaines.Elle revêt différentes formes et un cas apparemment simple peut cacher un phénomène complexe. Ses causes étant multiples, sa détection, sa mesure et sa maîtrise relèvent de compétences variées qui en font une affaire de spécialistes !

Ayez les bons réflexes et venez profitez de l’expertise du Cetim à l’occasion de cette journée, qui vous aidera à déjouer les pièges de la corrosion.

Pour savoir plus et s’inscrire : Journees-techniques/Corrosion

Fatigue Failure Analysis of a Cooling Fan Blade

Publié le par
Répondre

A paper published in  » Engineering Failure Analysis » on www.sciencedirect.com.

Fatigue failure of holding U-bolt of a cooling fan blade is analyzed. Fractography of the fracture surface reveals the characteristics of a fatigue fracture. Finite element modeling is used for stress analyzing. Analysis of the loading conditions indicates that the bolts are under multiaxial fatigue. ……..

Read more

Ruptures d’arbres épaulés clavetés (3)

Publié le par
Répondre

Avatar Cas ConcretsUn précédent article «Vintage» faisait état d’une règle pratique de positionnement établie au Cetim en 1977. Quatre fiches « Cas Concrets » illustraient cet publication. Cinq autres fiches sont venus précédemment compléter cet article.

Voici les trois dernières fiches «Cas Concrets» d’arbres épaulés clavetés rompus en fatigue. Elles avaient été publiées dans le numéro 55 d’avril 1978 de Cetim-Informations.

telecharger le doc

 

Vintage – Règle pratique du positionnement des rainures de clavetage

Publié le par
Répondre

Vintage Clavettes_arbres_epaulesRetrouver dans la Mécatech, du Cetim, dans la série « Vintage », un article sur le bon positionnement des rainures de clavette sur les arbres épaulés clavetés. Il est illustré de nombreux « Cas Concrets ».

Les différents articles de cette série «Vintage» ont été publiés dans la revue Cetim Informations dans les années 74 à 90. Bien qu’ils soient anciens, le contenu de ces articles est toujours d’actualité… Ils viennent en complément de la série «Cas concrets» consacrée à des fiches d’analyses de défaillances.