Metallurgical investigation of cracked aluminium alloy valve

1-s2-0-s2213290213000096-gr1A case study published in « Case Studies in Engineering Failure Analysis« , July 2013.

The high strength aluminium alloy Al–5.5Zn–2.5Mg–1.5Cu (AA7075) is being widely used in realisation of aerospace components. A component ‘fill and vent valve’ used in liquid propulsion system was fabricated from AA 7075 forgings in T7352 temper condition, and subsequently undergone various functional tests, four years back. Recently, during dye penetrant test after proof pressure test at 525 bar, a valve indicated presence of a crack. Detailed metallurgical investigation indicated that failure was caused by stress corrosion cracking.

Read more …

Laisser un commentaire

Entrez vos coordonnées ci-dessous ou cliquez sur une icône pour vous connecter:

Logo WordPress.com

Vous commentez à l'aide de votre compte WordPress.com. Déconnexion / Changer )

Image Twitter

Vous commentez à l'aide de votre compte Twitter. Déconnexion / Changer )

Photo Facebook

Vous commentez à l'aide de votre compte Facebook. Déconnexion / Changer )

Photo Google+

Vous commentez à l'aide de votre compte Google+. Déconnexion / Changer )

Connexion à %s