Undercutting Formation Mechanism in Gas Metal Arc Welding

2016-06-04_07h59_57A vision­based sensing system was improved to acquire 2D images of weld pool shape and tracer particle movement simultaneously. …..

Based on analysis of tracer particle movement, roles of different associated forces, such as gravity, arc drag force, Maragoni force, magnetic force, droplet impact, and viscous force, were investigated. The results show that liquid metal under the arc decreases to a thin liquid layer if the welding speed is more than 1.0 m/min. This phenomenon makes viscous resistance increase in the thin liquid layer, which impedes transverse spreading of liquid metal. Thus, it is difficult for the weld toe to be filled by molten metal. Meanwhile, experiments revealed the amount of forward molten metal can be ignored in the front and middle of the weld pool. Therefore, it is difficult for the weld toe to be filled by the backward molten metal. As a result, undercutting defects appear during high­speed welding……..

More

Laisser un commentaire

Entrez vos coordonnées ci-dessous ou cliquez sur une icône pour vous connecter:

Logo WordPress.com

Vous commentez à l'aide de votre compte WordPress.com. Déconnexion / Changer )

Image Twitter

Vous commentez à l'aide de votre compte Twitter. Déconnexion / Changer )

Photo Facebook

Vous commentez à l'aide de votre compte Facebook. Déconnexion / Changer )

Photo Google+

Vous commentez à l'aide de votre compte Google+. Déconnexion / Changer )

Connexion à %s