Fracture of a dental prosthesis from an inner thermal crack

A new paper about « Case study in Engineering Failure Analysis » published on ScienceDirect.com.

This paper describes the fractographic analysis of a veneer-ZrO2 single-unit dental prosthesis that fractured in a shell-like manner. Analysis of the retrieved fragment revealed that the crack originated in the bulk of the veneer from a thermal flaw located between two layers of the veneering material. Using the measured flaw plane it showed that the conditions of loading at fracture were complex and probably involved important tangential components.

Acceder article

Laisser un commentaire

Entrez vos coordonnées ci-dessous ou cliquez sur une icône pour vous connecter:

Logo WordPress.com

Vous commentez à l'aide de votre compte WordPress.com. Déconnexion / Changer )

Image Twitter

Vous commentez à l'aide de votre compte Twitter. Déconnexion / Changer )

Photo Facebook

Vous commentez à l'aide de votre compte Facebook. Déconnexion / Changer )

Photo Google+

Vous commentez à l'aide de votre compte Google+. Déconnexion / Changer )

Connexion à %s