Analysis of abnormal fatigue failure of forklift forks

A paper published in  » Engineering Failure Analysis » finded on ScienceDirect.com.

The analysis of an abnormal failure of forklift forks is presented in this work. The investigation results suggested that failure occurred due to fatigue mechanism followed by sudden overload fracture. The orientation of fatigue fracture indicates abnormal lifting operation, favouring crack initiation from outer fork area which is the compression designed zone. Moreover, various surface flaws and weakness areas (such as surface marks, decarburized microstructures and weld zones) identified on the outer fork zone, compromise fatigue strength inducing premature crack nucleation and fast growth towards final failure.

Read the article : click here

Laisser un commentaire

Entrez vos coordonnées ci-dessous ou cliquez sur une icône pour vous connecter:

Logo WordPress.com

Vous commentez à l'aide de votre compte WordPress.com. Déconnexion / Changer )

Image Twitter

Vous commentez à l'aide de votre compte Twitter. Déconnexion / Changer )

Photo Facebook

Vous commentez à l'aide de votre compte Facebook. Déconnexion / Changer )

Photo Google+

Vous commentez à l'aide de votre compte Google+. Déconnexion / Changer )

Connexion à %s